Due to the ever-increasing restrictions connected to the use of toxic lead-based materials, the developing of lead-free piezoceramics has become one of the most urgent tasks. In this context, potassium sodium niobate materials (KNN) have attracted a lot of interest as promising candidates due to their excellent piezo properties. For this reason, many efforts have been addressed to optimize the synthesis process now suffering by several drawbacks including the high volatilization of potassium and sodium at the conventional high temperature treatments and the use of expensive metal precursors. To overcome these issues, a new modified Pechini method to synthesize single phase K0.5Na0.5NbO3powders, from water soluble metal precursors, is presented. Microstructural and structural parameters are characterized by X-ray diffraction (XRD). Depending on the amount of citric acid added to the starting reagents, two pure single-phase K0.5Na0.5NbO3(2g citric acid) and K0.3Na0.7NbO3(0.2g citric acid), respectively, are obtained with a good crystallinity at a moderate temperature of 500Â°C. The piezo responses of the as calcined systems are tested by piezoresponse force microscopy (PFM). K0.5Na0.5NbO3exhibits a much higher response with respect to the other phase, which relates to the larger crystallinity and to the chemical composition.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
|Titolo:||Local Piezoelectric Behavior of Potassium Sodium Niobate Prepared by a Facile Synthesis via Water Soluble Precursors|
|Data di pubblicazione:||2018|
|Appare nelle tipologie:||1.1 Articolo in rivista|