A single high-entropy phase material with hexagonal structure is produced by a two-steps processing method. Elemental reactants are first remarkably converted by Self-propagating High-temperature Synthesis (SHS). The completion of the chemical transformation to the desired (Hf0.2Mo0.2Ta0.2Nb0.2Ti0.2)B2 phase and its concurrent consolidation up to 92.5% relative density is achieved by processing the SHS powders at 1950 °C via Spark Plasma Sintering. It is clearly evidenced that the use of the SHS technique is extremely beneficial to promote the formation of high-entropy ceramics, as compared to the time consuming ball milling treatment alternatively adopted.

Novel processing route for the fabrication of bulk high-entropy metal diborides / Tallarita, Giovanna; Licheri, Roberta; Garroni, Sebastiano; Orrù, Roberto; Cao, Giacomo. - In: SCRIPTA MATERIALIA. - ISSN 1359-6462. - 158:(2019), pp. 100-104. [10.1016/j.scriptamat.2018.08.039]

Novel processing route for the fabrication of bulk high-entropy metal diborides

Garroni, Sebastiano;
2019-01-01

Abstract

A single high-entropy phase material with hexagonal structure is produced by a two-steps processing method. Elemental reactants are first remarkably converted by Self-propagating High-temperature Synthesis (SHS). The completion of the chemical transformation to the desired (Hf0.2Mo0.2Ta0.2Nb0.2Ti0.2)B2 phase and its concurrent consolidation up to 92.5% relative density is achieved by processing the SHS powders at 1950 °C via Spark Plasma Sintering. It is clearly evidenced that the use of the SHS technique is extremely beneficial to promote the formation of high-entropy ceramics, as compared to the time consuming ball milling treatment alternatively adopted.
2019
Novel processing route for the fabrication of bulk high-entropy metal diborides / Tallarita, Giovanna; Licheri, Roberta; Garroni, Sebastiano; Orrù, Roberto; Cao, Giacomo. - In: SCRIPTA MATERIALIA. - ISSN 1359-6462. - 158:(2019), pp. 100-104. [10.1016/j.scriptamat.2018.08.039]
File in questo prodotto:
File Dimensione Formato  
Tallarita_et_al_Scripta_Mater_Revised_Unmarked.docx

accesso aperto

Tipologia: Documento in Post-print (versione referata ma senza layout editoriale)
Licenza: DRM non definito
Dimensione 1.81 MB
Formato Microsoft Word XML
1.81 MB Microsoft Word XML Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11388/220159
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 164
  • ???jsp.display-item.citation.isi??? 146
social impact